Hardness (Mohs): 3
Unit Volume Weight (Gr/cm3): 2.73
Density (Gr/cm3): 2.75
Water Absorption at Atmospheric Pressure (Weight%): 0.1
Boiling Water Absorption (Weight%): 0.1
Porosity . %: 0.2
more »»
Pressure Resistance (Kgf/cm2): 701
Compressive Strength After Freezing (Kgf/cm2): 590
Impact Resistance (Kgf/cm2): 23
Bending (Kgf/cm2): 151
Elastite Module (Kgf/cm2): 5.9 x 104
Occupancy Rate %: 99.3
Porosity Degree %: 0.7
Average Abrasion Strength (Cm3/50 cm2): 25.4
Average Tensile Strength (Kgf/cm2): 39

1 cm Minimum Thickness
3 - 6 m³ Block Dimension
3 Mohs Hardness
2.77 gr/cm³ Density
0.15 % Absorption
0.20 % Porosity
more »»
Slabs: 2 cm, 3 cm
Tiles: 12x12, 15x15, 18x18, 12x24 (inch)
Tiles: 30x30, 40x40, 45x45, 30x60 (cm)
Polished, Honed, Brushed
Straight, Beveled, Chiseled, Bullnose

Hardness (Mohs) 03.Nis
Unit Volume by Weight (gr/cm 3 ) 2,72
Density (gr/cm 3 ) 2,74
Water Absorption at Atmospheric Pressure By Weight(%0) 0,04
By Volume (%0) 0,109
Water Absorption at Boiling Water By Weight(%0) 0,053
more »»
By Volume (%0) 0,145
Porosity 0% 0,109
Compressive Strength (Kgf/cm 2 ) 721
Compressive Strength After Freezing (Kgf/cm 2 ) 651
Strength to Blow (Kgf/cm 2 ) 15,97
Strength to Bending (Kgf/cm 2 ) 122
Modules of Elasticity (Kgf/cm 2 ) 106,123
Ratio of Fullness 0% 99,3
Degree of Pores 0% 0,7
Average Abrasion Strength (cm 3 /50cm 2 ) 25,02
Average Tensile Strength, (Kgf/cm 2 ) 59
CHEMICAL ANALYSIS %
SiO2 0,02
Fe2O3 0,12
CaO 52,16
MgO 2,56

Hardness: 3 mohs
Unit Volume Weight: 2,71 gr/cm3
Density: 2,73 gr/cm3
Porosity: 0,2%
Compressive strength: 704 kgf/cm2
Strength to blow: 17 kgf/cm2
more »»
Strength to bending: 111 kgf/cm2
Modules of elasticity: 56500 kgf/cm2
Ratio of fullness: 99,3 %
Degree of pores: 0,7%
Average abrasion: 29,6 cm3/50cm2
Average tensile strength: 65 kgf/cm2